weak lamination: this kind of bad phenomenon often occurs in the printing lamination with large area and large ink level. The main manifestations are: after die-cutting, the edge of the laminated film is opened and warped, the die-cutting indentation line and the embossing reverse white. Ironing and embossing reverse white, etc. The reasons for this are:

1. The solid content of the glue is low or the amount of glue is small, so that it cannot be well attached to the printing paper! The weak lamination caused by this situation is easy to fall off no matter what material it is, or what kind of pictures and texts are printed. Especially for some paper with large printing powder and not smooth surface and special film with thick film material, the selected glue also has certain requirements. For our " shiny starry frosted lamination film", 

 which is suggested to use high viscosity embossing glue!

2. When printing, the ink is not completely dried or the solidity after drying is not good, that causes the film reverse white. It is recommended to wait for 4-8 hours after printing, so that the ink on the surface of the printed sheet is completely cured and dried before laminating.

3. The surface tension of the printing material is too low, which leads to the weak adhesion of the ink and the weak lamination. It is recommended to consider online corona or primer coating to increase the surface tension of the material before printing.

4. In order to achieve high-quality results for the surface lamination of products with large area, large ink level and high requirements, it is recommended to adjust the appropriate amount of glue, temperature, speed and tension before the formal lamination